PRODUCT NAME  Epoxy Coating SLH100-2

BRIEF  Two Pack Solvent-free Wear proof High Build Can be coated Self-curing Epoxy Coating

FEATURES
-Excellent resistance to Impact and cathodic disbonding
-Excellent adhesion, abrasion resistance, water resistance, resistance to chemical corrosion and cathodic  protection, good coordination in ocean tidalrange zone and splash zone, severe corrosive environment, corrosion protection "can reach more than 30 years, Good construction performance, coating a dry film thickness is 500 microns, and can greatly save construction time and cost
-Solvent-free, No environmental hazards
-Good cure properties of low temperature , High pressure airless spray

RESISTANCE GUIDE

HEAT RESISTANCE  Up to 140℃ dry heat
WEATHERABILITY   Some chalking and yellowing will occur with exterior exposure, however this will not detract from the resistance properties of the coating
SOLVENTS         Resists splash and spillage of most varsol, refined petroleum products
ACIDS                 Suitable for splash and spillage to common acids
ALKALIS             Suitable for splash and spillage to strong alkalis
SALTS                 Excellent resistance to neutral and alkali salts
WATER               Excellent resistance to immersion in fresh and salt water
ABRASION         Good when fully cured.

USES:Widely used on Steel structure or concrete pile in dry-wet alternation, such as severe corrosive environment of Offshore platform, steel pile wharf, port facilities, Bridges, Marine, tidal flat, inland rivers for long-term.

TYPICAL PROPERTIES AND APPLICATION DATA
COLOR                        Grey  Red  Half  matt  gloss
DENSITY                       1.8g/cm3
SOLIDS BY VOLUME              ≥99.5% (mixture)
SOLIDS BY WEIGHT               99%
SPREADING RATE                1.1 m2/kg   (500um DFT)
DRYING TIME(23℃)              Touch  2 Hr    Handle  24 Hr    Full cure 7Days
OVERCOAT INTERVAL(23℃)        Min 8 Hr   Max 7 Days 
STORAGE                       at least 12 months (dry, cool and under cover )
PACKAGING                     Part A: 20kg/ bucket   Part B: 4(5)kg/ bucket
MIXING RATIO (M/M)             Part A : Part B=5:1 or 4:1
CURE TIME(23℃)                none
POT LIFE(23℃)                  1 Hr

DIRECTIONS Before using stir or using dynamic mixer mixing two components completely,Just mix a good raw material and mixing of raw materials before can not be together. Rate of cure will vary depending on temperature and other factors such as ventilation, film thickness, humidity, thinner. The temperature of stir will >15℃, otherwise thinner should be added for needed viscosity after stir.
Overmuch thinner will lead sag and slow cure rate, thin film, thinner should be added after mixed. Practical spreading rates may be reduced 5%—25% for wastage of different application conditions.

APPLICATION 

STEEL: Steel surface must be prepared by abrasive blast cleaning to ISO Standard Class Sa2.5 or power tool cleaning Class St3. The surface coated by shop primer should be dry, clean and no dirt, take the second descaling where film damaged or corrosion, and achieve Sa2.5 level or St3 level. Clear the zinc salt with high pressure fresh water or  sand . Weld and the damage parts processing to Sa2.5 level or St3 level.
Don’t apply at temperatures below 5℃ or above 40℃. Don’t apply at relative humidity above 85% or when the surface is less than 3℃ above the dew point.
Don’t apply if there is fog, rain, snow or strong wind.
BRUSH/ROLLER: Suitable for small areas only. Apply even coats of the mixed material to the prepared surface. Thin if necessary with up to 0-5% with Epoxy Thinner X-100. Additional coats may be required to attain specified thickness.
CONVENTIONAL SPRAY: Thinning is not normally required, however 0-5% of Epoxy Thinner X-100 can be added.
AIRLESS SPRAY: Thinning is not normally required, however 0-5% of Epoxy Thinner X-100 can be added. Pump ratio is 32:1 or 45:1 and fluid tip is 0.43-0.48 mm.
Overcoating: Aged coating should be tested for lifting by a method such as ‘X’cut or crosshatch methods. If it lifts, remove it. The surface must be free of oil, grease and other contaminants.
Previous coat: Zinc Rich Epoxy Primer, Anticorrosive Epoxy Primer
CLEAN UP: with Epoxy Thinner X-2

SAFETY:Pay attention to the safety precautions before and after using this product. Users should comply with the provision of the respective country or local government. It’s dangerous or deadly to eating it. To avoid inhalation of thinner steams and spray mists.
Use protective wears correctly; the skin and eyes should avoid contacting it. Use with good ventilation. This product is flammable. All sources of ignition must be eliminated in, or near the working area. DO NOT SMOKE. Fight fire with foam, CO2 or dry chemical powder. On burning will emit toxic fumes.

Notes: The data in the manual is get from standard experiments and may be vary from different conditions in use. Please refer to the latest manual if the data is altered and we would not inform specially.

 